Effect of Application Deviations on Dentin Sealing of a Universal Adhesive: Permeability and Nanoleakage
Autor*innen
Abstract
Objective The objective of this study was to evaluate the effect that deviations from the recommended protocol of a universal adhesive system, applied to dentin according to the self-etch (SE) and the etch-and-rinse (ER) techniques, has on permeability and nanoleakage.
Materials and Methods Permeability: 60 extracted non-carious human third molars (N = 60) were sectioned to obtain 0.7-mm-thick dentin disks. The specimens were randomly assigned to three subgroups and treated with a universal adhesive system (Prime&Bond Active Universal) using the SE and ER techniques: (1) following the manufacturer's instructions with 5 seconds drying (MFR DRY 5S), (2) following the MFR DRY 10S, and (3) reduced application time of the adhesive to 5 seconds (APPL 5S). Nanoleakage: 12 additional 0.7-mm-thick dentin disks were prepared, treated and divided into six groups. They were immersed in 50 wt% ammoniacal silver nitrate and processed according to conventional methods for the analysis of nanoleakage under transmission electron microscopy.
Statistical Analysis The results were statistically analyzed by two-way analysis of variance and post-hoc Bonferroni's test.
Results Significant differences in permeability reduction were observed among the treatment groups (0.001). The results obtained for APPL 5S were significantly lower than the results obtained for both the MFR DRY 5S (p = 0.003) and MFR DRY 10S (p = 0.001).
Conclusions The reduced application time to 5 seconds creates imperfect dentin tubule sealing, which may explain clinical reports of postoperative sensitivity and early degradation of the resin–dentin interface.
Keywords
dentin tubule sealing - etch-and-rinse - nanoleakage - self-etch - TEM - universal adhesivesPublikationsverlauf
Artikel online veröffentlicht:
11. Juli 2022
© 2022. The Author(s). This is an open access article published by Thieme under the terms of the Creative Commons Attribution License, permitting unrestricted use, distribution, and reproduction so long as the original work is properly cited. (https://creativecommons.org/licenses/by/4.0/)
Thieme Medical and Scientific Publishers Pvt. Ltd.
A-12, 2nd Floor, Sector 2, Noida-201301 UP, India
-
References
- 1 Cruz J, Silva A, Eira R, Sousa B, Lopes M, Cavalheiro A. Dentin permeability and nanoleakage of universal adhesives in etch-and-rinse vs self-etch modes. Oper Dent 2021; 46 (03) 293-305
- 2 Lima JFM, Wajngarten D, Islam F, Clifford J, Botta AC. Effect of adhesive mode and chlorhexidine on microtensile strength of universal bonding agent to sound and caries-affected dentins. Eur J Dent 2018; 12 (04) 553-558
- 3 Vieira BR, Dantas ELA, Cavalcanti YW, Santiago BM, Sousa FB. Comparison of self-etching adhesives and etch-and-rinse adhesives on the failure rate of posterior composite resin restorations: a systematic review and meta-analysis. Eur J Dent 2021; (e-pub ahead of print)
- 4 Kanniappan G, Hari P, Jujare RH. Comparative evaluation of resin dentin interface using universal and total- etch adhesive systems on sound and eroded dentin: in vitro study. Eur J Dent 2022; 6 (01) 153-160
- 5 Bouillaguet S, Duroux B, Ciucchi B, Sano H. Ability of adhesive systems to seal dentin surfaces: an in vitro study. J Adhes Dent 2000; 2 (03) 201-208
- 6 Frankenberger R, Krämer N, Petschelt A. Technique sensitivity of dentin bonding: effect of application mistakes on bond strength and marginal adaptation. Oper Dent 2000; 25 (04) 324-330
- 7 Peutzfeldt A, Asmussen E. Adhesive systems: effect on bond strength of incorrect use. J Adhes Dent 2002; 4 (03) 233-242
- 8 Armstrong SR, Keller JC, Boyer DB. The influence of water storage and C-factor on the dentin-resin composite microtensile bond strength and debond pathway utilizing a filled and unfilled adhesive resin. Dent Mater 2001; 17 (03) 268-276
- 9 Sahin C, Cehreli ZC, Yenigul M, Dayangac B. In vitro permeability of etch-and-rinse and self-etch adhesives used for immediate dentin sealing. Dent Mater J 2012; 31 (03) 401-408
- 10 Sano H, Yoshiyama M, Ebisu S. et al. Comparative SEM and TEM observations of nanoleakage within the hybrid layer. Oper Dent 1995; 20 (04) 160-167
- 11 Tao L, Pashley DH. The relationship between dentin bond strengths and dentin permeability. Dent Mater 1989; 5 (02) 133-139
- 12 Li H, Burrow MF, Tyas MJ. Nanoleakage of cervical restorations of four dentin bonding systems. J Adhes Dent 2000; 2 (01) 57-65
- 13 Tay FR, Pashley DH, Yiu C. et al. Nanoleakage types and potential implications: evidence from unfilled and filled adhesives with the same resin composition. Am J Dent 2004; 17 (03) 182-190
- 14 Brännström M. Etiology of dentin hypersensitivity. Proc Finn Dent Soc 1992; 88 (Suppl. 01) 7-13
- 15 Prati C, Pashley DH. Dentin wetness, permeability and thickness and bond strength of adhesive systems. Am J Dent 1992; 5 (01) 33-38
- 16 Prati C. What is the clinical relevance of in vitro dentine permeability tests?. J Dent 1994; 22 (02) 83-88
- 17 Kolker JL, Vargas MA, Armstrong SR, Dawson DV. Effect of desensitizing agents on dentin permeability and dentin tubule occlusion. J Adhes Dent 2002; 4 (03) 211-221
- 18 Yiu CK, Hiraishi N, Chersoni S. et al. Single-bottle adhesives behave as permeable membranes after polymerisation. II. Differential permeability reduction with an oxalate desensitiser. J Dent 2006; 34 (02) 106-116
- 19 Goodis HE, Marshall Jr GW, White JM, Gee L, Hornberger B, Marshall SJ. Storage effects on dentin permeability and shear bond strengths. Dent Mater 1993; 9 (02) 79-84
- 20 Ozok AR, Wu MK, Wesselink PR. The effects of post-extraction time on the hydraulic conductance of human dentine in vitro. Arch Oral Biol 2002; 47 (01) 41-46
- 21 Pashley DH, Depew DD. Effects of the smear layer, Copalite, and oxalate on microleakage. Oper Dent 1986; 11 (03) 95-102
- 22 Cavalheiro A, Cruz J, Sousa B. et al. Dentin adhesives application deviations: effects on permeability and nanoleakage. Dent Mater J 2021; 40 (05) 1160-1168
- 23 Pashley DH, Carvalho RM, Pereira JC, Villanueva R, Tay FR. The use of oxalate to reduce dentin permeability under adhesive restorations. Am J Dent 2001; 14 (02) 89-94
- 24 Tay FR, Pashley DH. Water treeing—a potential mechanism for degradation of dentin adhesives. Am J Dent 2003; 16 (01) 6-12
- 25 Faul F, Erdfelder E, Buchner A, Lang AG. Statistical power analyses using G*Power 3.1: tests for correlation and regression analyses. Behav Res Methods 2009; 41 (04) 1149-1160
- 26 Faul F, Erdfelder E, Lang AG, Buchner A. G*Power 3: a flexible statistical power analysis program for the social, behavioral, and biomedical sciences. Behav Res Methods 2007; 39 (02) 175-191
- 27 Pashley D. Dentin permeability: theory and practice. In: Spangberg LSW. ed. Experimental Endodontics. Raton, FL: CRC Press Boca; 1990: 20-46
- 28 Tay FR, Pashley DH, Garcìa-Godoy F, Yiu CK. Single-step, self-etch adhesives behave as permeable membranes after polymerization. Part II. Silver tracer penetration evidence. Am J Dent 2004; 17 (05) 315-322
- 29 Tay FR, Pashley DH, Suh B, Carvalho R, Miller M. Single-step, self-etch adhesives behave as permeable membranes after polymerization. Part I. Bond strength and morphologic evidence. Am J Dent 2004; 17 (04) 271-278
- 30 Cruz J, Sousa B, Coito C, Lopes M, Vargas M, Cavalheiro A. Microtensile bond strength to dentin and enamel of self-etch vs. etch-and-rinse modes of universal adhesives. Am J Dent 2019; 32 (04) 174-182
- 31 Cadenaro M, Antoniolli F, Sauro S. et al. Degree of conversion and permeability of dental adhesives. Eur J Oral Sci 2005; 113 (06) 525-530
- 32 Cuevas-Suárez CE, da Rosa WLO, Lund RG, da Silva AF, Piva E. Bonding performance of universal adhesives: an updated systematic review and meta-analysis. J Adhes Dent 2019; 21 (01) 7-26
- 33 Hanabusa M, Mine A, Kuboki T. et al. Bonding effectiveness of a new ‘multi-mode’ adhesive to enamel and dentine. J Dent 2012; 40 (06) 475-484
- 34 Nagura Y, Tsujimoto A, Fischer NG. et al. Effect of reduced universal adhesive application time on enamel bond fatigue and surface morphology. Oper Dent 2019; 44 (01) 42-53
- 35 Saikaew P, Matsumoto M, Chowdhury A, Carvalho RM, Sano H. Does shortened application time affect long-term bond strength of universal adhesives to dentin?. Oper Dent 2018; 43 (05) 549-558
- 36 Cavalheiro A, Vargas MA, Armstrong SR, Dawson DV, Gratton DG. Effect of incorrect primer application on dentin permeability. J Adhes Dent 2006; 8 (06) 393-400
- 37 Ozok AR, Wu MK, Wesselink PR. Comparison of the in vitro permeability of human dentine according to the dentinal region and the composition of the simulated dentinal fluid. J Dent 2002; 30 (2-3): 107-111
- 38 Tagami J, Hosoda H, Burrow MF, Nakajima M. Effect of aging and caries on dentin permeability. Proc Finn Dent Soc 1992; 88 (Suppl. 01) 149-154
- 39 Kusunoki M, Itoh K, Hisamitsu H, Wakumoto S. The efficacy of dentine adhesive to sclerotic dentine. J Dent 2002; 30 (2-3): 91-97
- 40 Perdigão J. Dentin bonding-variables related to the clinical situation and the substrate treatment. Dent Mater 2010; 26 (02) e24-e37